Hollow glass Microsphere is a kind of hollow spherical powdery ultra-light inorganic non-metallic material. Its true density is 0.15-0.65g/cm³, particle size is 2-120μm, wall thickness is 1-2μm, and its compressive strength ranges 3-125MPa, it has the characteristics of light weight, large volume, low thermal conductivity, high compressive strength, and good fluidity. It is a product filler and lightening agent in paint coatings, rubber, modified plastics, glass fiber reinforced plastic, artificial stone, putty and other industries; In oil and gas field mining industries it can be used to produce cement slurry and drilling fluid with properties of high strength, high compressive,low density.

Properties:

Pure white color, Hollow Glass Microsphere can be widely used in products which have high requirements for looks and colors.
Low density, reducing the products’ basic weight obviously after filling. (the density is one out of a dozen of traditional filler particles’ density). Relatively large volume, which can substitute and save more resins, reducing cost.

High dispersion and good fluidity, dimensional stability, reduced warpage and shrinkage when used as additives.
Heat insulation, sound insulation, mostly used as heat insulation paints and coatings, automotive sealants.
In addition, corrosion resistant, fire resistant, non-conducting.

Chemical composition(%):

SiO2	58-71
Na2CO3	12-25
B2O3	3-12
Al2O3	0-10
CaO	0.2-1.0
Fe2O3	0-0.5
MgO	0-0.05

Physical Index:

True Density	0.18-0.60g/cm3
Bulk Density	0.10-0.34g/cm3
Crush Strength	4-125Mpa/500-18000Psi
Survival	Min 90%
Flotation	Min 92%
Moisture	Max 0.5%
Particle Size	D50:20-70um
Max. Particle Size:	200um
Melting Point	1600°C

Specifiction

Spec.	True Density(g/cm3)	Bulk Density(g/cm3)	Compressive strength(Mpa/Psi)	D50(um)	D90(um)	Packing(Kgs)
HL15	0.13-0.17	0.08-0.09	4/500	65	120	8
HL20	0.20-0.22	0.10-0.12	4/500	65	110	10
HL25	0.24-0.27	0.13-0.15	5/750	65	100	12.5
HL30	0.29-0.32	0.15-0.18	10/1500	55	85	15
HL32	0.31-0.33	0.17-0.19	14/2000	45	80	15
HL35	0.33-0.37	0.18-0.21	21/3000	40	70	15
HL38	0.37-0.39	0.19-0.22	38/5500	40	65	20
HL40	0.39-0.42	0.19-0.23	28/4000	40	70	20
HL42	0.41-0.44	0.21-0.24	55/8000	40	60	20
HL46	0.44-0.48	0.23-0.26	41/6000	40	70	22.5
HL50	0.48-0.52	0.25-0.27	55/8000	40	60	25
HL55	0.53-0.55	0.27-0.29	68/10000	40	60	25
HL60	0.58-0.62	0.29-0.34	83/12000	40	65	30
HL60S	0.58-0.63	0.30-0.34	125/18000	35	55	30
HS38	0.37-0.39	0.19-0.22	38/5500	30	50	20
HM10	1.4-1.6	0.45-0.50	193/28000	5	10	30
HM15	1.2-1.3	0.40-0.45	124/18000	7	15	30
HM20	1.05-1.15	0.39-0.44	124/18000	9	20	25
HM30	0.9-1.0	0.35-0.4	83/12000	14	30	25
HS20	0.18-0.22	0.10-0.12	7/1000	60	90	10
HS22	0.20-0.24	0.11-0.13	8/1200	45	70	10
HS28	0.27-0.30	0.15-0.17	28/4000	45	65	15
HS38	0.36-0.40	0.19-0.22	38/5500	30	50	20
HS42	0.40-0.44	0.21-0.24	55/8000	25	40	20
HS46	0.44-0.50	0.22-0.25	110/16000	20	30	22.5
HS60	0.58-0.62	0.29-0.33	193/28000	16	25	30
HS65	0.63-0.67	0.30-0.33	207/30000	13	20	32
HS70	0.75-0.80	0.33-0.35	207/30000	10	15	35

Application:

경량 시멘트, 저밀도 유정 시멘팅 슬러리 및 저밀도 시추 유체 첨가제.
저밀도 FRP(유리섬유 강화 플라스틱), SMC, BMC 복합재.
무게 감소용 나일론, PA, PA6, PA66.
저밀도 접착제 및 실란트.
단열 페인트 및 코팅제.
건설(뒤틀림/수축 감소).
단열 및 부력.
인조 대리석.

속이 빈 유리 미세구는 페인트 및 코팅제, 건축용 실란트, 고무, 플라스틱, FRP, 인조석, 퍼티 및 기타 제품에 충전제 및 경량화제로 사용될 수 있습니다. 또한, 이 유리 기포는 고강도 저밀도 시멘트 슬러리 및 석유·가스 추출 산업에서 저밀도 시추 유체를 생산하는 데에도 사용될 수 있습니다. 현재 점점 더 많은 산업 분야에서 제품의 특성을 개선하기 위한 첨가제로서 속이 빈 유리구를 시험하고 있습니다.

패키지:

패키지 1 패키지 2

TDS가 업로드되지 않았습니다

MSDS가 업로드되지 않았습니다

제품

무게 감소를 위해 어류 부표에 속이 빈 유리 미세구슬을 첨가했습니다.

Properties:

Chemical composition(%):

Physical Index:

연관 상품

경량 단열재용 속이 빈 유리 미세구체

속이 빈 유리 미세구